Kit consists of 1kg of PART A and 1kg of PART B
Total kit volume 1.88 Litres
PART A is a cream liquid and PART B is a amber liquid that have virtually no odour and react to form a strong, tough, non-greasy polyurethane plastic white in colour.
The colour of the cured plastic can be changed with the addition of a colour pigment to part A prior to mixing the two components. We have a range of compatible colour pigments here
This product has a simple mixing ratio of 1:1 by weight. Please note the two liquids have different densities hence different volumes which is why the mixing ratio is equal parts by weight not volume.
The pot life is approximately 5 minutes and the casting can generally be de-moulded in 30-45 minutes depending on the size of the casting.
The liquid mixture has a very low viscosity of 69 mPas enabling it to flow in fine details and deep undercuts whilst also minimizing bubbles.
Once cured it has both a good tensile and a good flexural strength making it excellent for prototypes, scale models, toys and producing detailed decorative objects etc.
The cure profile of this resin is unsuitable for roto/slush casting for a suitable resin click here
|Properties ||Units ||White |
|Pot Life (25°C) ||Minutes ||5 |
|Demould Time (25°C) ||Minutes ||30-45 |
|Viscosity (25°C) ||Mpa.s ||69 |
|Density (25°C) ||g/cm3 ||1.06 |
|Hardness ||Shore D ||73 |
|Linear Shrinkage ||% ||0.05 |
|Flexural Strength ||Mpa ||33 |
|Flexural Modulus ||Mpa ||1060 |
|Tensile Strength ||Mpa ||24 |
|Elongation at Break ||% ||8 |
|Heat Distortion ||°C ||90 |
Technical Data Sheet Safety Data Sheet PART A Safety Data Sheet PART B