Kit consists of 200g of PART A and 90g of PART B
Total kit volume 268ml
PART A is a cream liquid and PART B is a amber liquid that have virtually no odour and react to form a strong, tough, very hard polyurethane rubber white in colour. This product has a hardness comparable to trolly and roller skate wheel etc.
The colour of the cured plastic can be changed with the addition of a colour pigment to part A prior to mixing the two components. We have a range of compatible colour pigments here
This product has a mixing ratio of 100:45 by weight.
The fast versions pot life is approximately 6-7 minutes and the casting can generally be de-moulded in 1-2 hours depending on the size and especially the thickness of the casting.
The slow versions pot life is approximately 20 minutes and the casting can generally be de-moulded in 3-5 hours depending on the size and especially the thickness of the casting.
| Properties | Units | |
| Pot Life (25°C) | Minutes | 6-7 or 20 |
| Demould Time (25°C) | Hours | 1-2 or 3-5 |
| Viscosity (25°C) | Mpa.s | 670 |
| Density (25°C) | g/cm3 | 1.08 |
| Hardness | Shore A | 90 |
| Linear Shrinkage | % | 0.05 |
| Flexural Strength | Mpa | - |
| Flexural Modulus | Mpa | - |
| Tensile Strength | Mpa | - |
| Elongation at Break | % | - |
| Heat Distortion | °C | 80 |