Kit consists of 200g of PART A and 80g of PART B
Total kit volume 256ml
PART A is a cream liquid and PART B is a amber liquid that have virtually no odour and react to form a strong, tough, flexible polyurethane rubber white in colour. This product is firmer in hardness compared to natural rubber used in vehicle bushes/bump stops, seals and matting etc so can be used in the production of stiffer uprated polyurethane replacement parts commonly known as sports poly bushes. To produce parts in a similar hardness to the original natural rubber use our Shore A65.
The colour of the cured plastic can be changed with the addition of a colour pigment to part A prior to mixing the two components. We have a range of compatible colour pigments here
This product has a mixing ratio of 100:40 by weight.
The fast versions pot life is approximately 6-7 minutes and the casting can generally be de-moulded in 1-2 hours depending on the size and especially the thickness of the casting.
The slow versions pot life is approximately 20 minutes and the casting can generally be de-moulded in 3-5 hours depending on the size and especially the thickness of the casting.
Properties | Units | |
Pot Life (25°C) | Minutes | 6-7 or 20 |
Demould Time (25°C) | Hours | 1-2 or 3-5 |
Viscosity (25°C) | Mpa.s | 600 |
Density (25°C) | g/cm3 | 1.08 |
Hardness | Shore A | 80 |
Linear Shrinkage | % | 0.05 |
Flexural Strength | Mpa | - |
Flexural Modulus | Mpa | - |
Tensile Strength | Mpa | - |
Elongation at Break | % | - |
Heat Distortion | °C | 80 |
Technical Data Sheet Safety Data Sheet PART A Safety Data Sheet PART B