Kit consists of 10kg of PART A and 10kg of PART B
Total kit volume 18.518 Litres
PART A is a cream liquid and PART B is a amber liquid that have virtually no odour and react to form a strong, tough, non-greasy polyurethane rigid plastic beige in colour.
The colour of the cured plastic can be changed with the addition of a colour pigment to part A prior to mixing the two components. We have a range of compatible colour pigments here
This product has a simple mixing ratio of 1:1 by weight. Please note the two liquids have different densities hence different volumes which is why the mixing ratio is equal parts by weight not volume.
There's a choice of two cure speeds. A 3-4 minute pot life where the casting can generally be de-moulded in 30-40 minutes or a 6 minute pot life with a 1-2 hour de-mould time depending on the size of the casting.
The liquid mixture has a very low viscosity of 50 mPas enabling it to flow in fine details and deep undercuts whilst also minimizing bubbles.
Once cured it is the strongest of all our resins, having both a high tensile and a high flexural strength making it excellent for prototypes, scale models, toys and producing detailed decorative objects etc.
The cure profile of this resin is unsuitable for roto/slush casting for a suitable resin click here
|Properties ||Units ||Beige |
|Pot Life (25°C) ||Minutes ||3-4 |
|Demould Time (25°C) ||Minutes ||30-40 |
|Viscosity (25°C) ||Mpa.s ||50 |
|Density (25°C) ||g/cm3 ||1.08 |
|Hardness ||Shore D ||70-75 |
|Linear Shrinkage ||% ||0.05 |
|Flexural Strength ||Mpa ||55 |
|Flexural Modulus ||Mpa ||1100 |
|Tensile Strength ||Mpa ||33 |
|Elongation at Break ||% ||7-8 |
|Heat Distortion ||°C ||70-75 |