Kit consists of 2.5kg of PART A and 2.5kg of PART B
Total kit volume 4.54 Litres
PART A is a cream liquid and PART B is an amber liquid that have virtually no odour and react to form a strong, tough, non-greasy polyurethane plastic beige in colour.
The colour of the cured plastic can be changed with the addition of a colour pigment to part A prior to mixing the two components. We have a range of compatible colour pigments here
This product has a simple mixing ratio of 1:1 by weight. Please note the two liquids have different densities hence different volumes which is why the mixing ratio is equal parts by weight not volume.
The pot life is approximately 12-14 minutes and the casting can generally be de-moulded in one hour depending on the size of the casting.
The liquid mixture has a very low viscosity of 158 mPas enabling it to flow in fine details and deep undercuts whilst also minimizing bubbles.
Once cured it has both a good tensile and a high flexural strength making it excellent for prototypes, scale models, toys and producing detailed decorative objects etc.
The cure profile of this resin is unsuitable for roto/slush casting please
|Properties ||Units ||Slow Curing |
|Pot Life (25°C) ||Minutes ||12-14 |
|Demould Time (25°C) ||Hours ||2-4 |
|Viscosity (25°C) ||Mpa.s ||158 |
|Density (25°C) ||g/cm3 ||1.08 |
|Hardness ||Shore D ||72 |
|Linear Shrinkage ||% ||0.05 |
|Flexural Strength ||Mpa ||50 |
|Flexural Modulus ||Mpa ||1380 |
|Tensile Strength ||Mpa ||28 |
|Elongation at Break ||% ||5 |
|Heat Distortion ||°C ||70 |