Kit consists of 500g of PART A and 500g of PART B
Total kit volume 909ml
PART A is a cream liquid and PART B is an amber liquid that have virtually no odour and react to form a strong, tough, non-greasy polyurethane plastic beige in colour.
The colour of the cured plastic can be changed with the addition of a colour pigment to part A prior to mixing the two components. We have a range of compatible colour pigments here
This product has a simple mixing ratio of 1:1 by weight. Please note the two liquids have different densities hence different volumes which is why the mixing ratio is equal parts by weight not volume.
The pot life is approximately 12-14 minutes and the casting can generally be de-moulded in one hour depending on the size of the casting.
The liquid mixture has a very low viscosity of 158 mPas enabling it to flow in fine details and deep undercuts whilst also minimizing bubbles.
Once cured it has both a good tensile and a high flexural strength making it excellent for prototypes, scale models, toys and producing detailed decorative objects etc.
The cure profile of this resin is unsuitable for roto/slush casting please
| Properties | Units | Slow Curing |
| Pot Life (25°C) | Minutes | 12-14 |
| Demould Time (25°C) | Hours | 2-4 |
| Viscosity (25°C) | Mpa.s | 158 |
| Density (25°C) | g/cm3 | 1.08 |
| Hardness | Shore D | 72 |
| Linear Shrinkage | % | 0.05 |
| Flexural Strength | Mpa | 50 |
| Flexural Modulus | Mpa | 1380 |
| Tensile Strength | Mpa | 28 |
| Elongation at Break | % | 5 |
| Heat Distortion | °C | 70 |