Black Polyurethane Fast Cast Resin 2kg Kit
BEST

Black Polyurethane Fast Cast Resin 2kg Kit

£27.00

Kit consists of 1kg of PART A and 1kg of PART B

Total kit volume 1.92 Litres  

Please note that the two liquids have different densities so though they weigh the same their volumes are different.


  • Minerals fillers can be added to increase the volume or weight  
  • Can be made into a thixotropic paste 
  • Metallic Fillers can be added so the casting appears to be made from a metal 
  • Can be painted
  • Very Low viscosity
  • Excellent fine detail reproduction
  • Simple mix ratio of 100 : 100 by weight 

PART A is a black liquid and PART B is a dark amber liquid that react to form a black plastic. Once cured it has both a high tensile and flexural strength. Contains a filler that helps minimize bubbles by absorbing Co2 gas produced when moisture in the air introduced when mixing the two parts reacts with the resin. This resin is unsuitable for roto/slush casting.

 


PROPERTIES UNITS LOW ODOUR
Viscosity (25°C) Mpa.s 50
Density (25°C) g/cm3 1.08
Pot Life                (200g @ 25°C) Minutes 3-4
Demould Time            (200g @ 25°C) Minutes 30-40
Hardness Shore D 70-75
Linear Shrinkage % 0.05
Flexural Strength Mpa 55
Flexural Modulus Mpa 1100
Tensile Strength Mpa 33
Elongation at Break % 7-8
Heat Distortion °C 60-65

 FILLITE FILLER  

Lightweight, hollow, spherical, low density, free-flowing, alumino-silicate microspheres which when added at 50% of the weight of the resin will increase the volume of the resin by 100-150% and remain pourable.


FUMED SILICA FILLER  

Thixotropic additive, when added to the resin at 5% creates a paste that can be brushed or spread into or on to moulds to create hollow casts.


METAL FILLERS FOR COLD CASTING  

An initial layer of a resin and metal filler mix are applied to the surface of the mould then the mould can be back filled with non metal filled resin. Once cured the cast piece is carefully polished with fine wire wool to bring out the finish of the metal. The higher the ratio of metal filler to resin used the higher the quality of the finish.

A more efficient method if using a silicone mould is to cover the surface of the mould in the powder, turn over and tap. A thin layer will stick to the surface and the excess will fall off which can be collected and used again.  Very gently pour in the resin being careful not to disturb the powder. The resin will soak into the powder leaving a very thin dense layer of metal on the surface of the cast that can then be polished.